Kaneka LG PVC Paste Resin LK170 170G 170L
PVC Resins are classified by their K-Value, an indicator of the molecular weight and degree of polymerization.
• K70-75 are high K value resins which gives best mechanical properties but are more difficult to process. They need more Plasticizer for same softness. High performance Cable insulations in Suspension Resin and tough coatings for Conveyor belts, Industrial Flooring and similar high end applications in Paste grade are some popular application. It is the costliest.
• K65-68 are medium K value resin which are the most popular. They have a good balance of Mechanical properties and processibility. UPVC (Unplasticised or Rigid PVC) is made from the less porous grades while Plasticised Applications are best made from the more porous grades. There is a lot of grade choice as they cater to the Majority of PVC applications. Because of its sheer volume this family of PVC resins are priced the lowest.
• K58-60 are low K-value ranges. Mechanical properties are lowest, but processing is easiest. Many difficult to process applications like injection moulding, blow moulding and Clear Calendered packaging film are made from the lower K value ranges. Prices are higher than Medium K Value Resins.
• K50-55 are special resins which are tailor made for some demanding applications. Interesting ones are Battery Separator Resins and Blending resins used along withPaste Grade resin to reduce costs. Processing is easiest.
As PVC is 56% Chlorine, it is one of the few Polymers which are self extinguishing, as Chlorine is a strong Flame inhibitor.
Besides, we also have PVC Paste, Titanium Dioxide, Iron Oxide Pigment, Carbon Black, Chrome Yellow, Chrome Green etc to colorful your PVC products.
Specification:
PVC RESIN PASTE TDS:
| Parameter | Grade |
| Standard: GB15592-2008 | 1156 | 1302 | 1702 |
| K - Value | 67 | 70 | 78 |
| Viscidity, ml/g | 100-120 | 115-135 | 154-174 |
| Polymerizing Index | 900-1150 | 1100-1350 | 1700-1950 |
| Volatile component, % ≤ | 0.4 | 0.4 | 0.5 |
| Paste thickening rat (24h)/ ≤ % | 100 | 100 | 100 |
| B-typeviscosity /Pa.s | 6.0-10.0 | ≤4.0 | ≤4.0 |
| Sieve residue %, mg/kg | 250um ≤ | 0 | 0 | 0 |
| 63um ≤ | 0.1 | 0.1 | 1.0 |
| VCM Residue PPM ≤ | 5 | 5 | 10 |
| Whiteness (160°C,10min)/ % ≥ | 80 | 80 | 76 |
| Number of impurity particles ≤ | 12 | 12 | 20 |
| Scraper fineness um ≤ | 100 | 100 | 100 |
Pvc Resin TDS
| | |
| | | | | |
| | | | | |
| | | | | |
Number of impurity particles ≤ | | | | |
Volatile content (incl. water) % ≤ | | | | |
| | | | | |
| | | | | | |
| | | | | |
Number of Fish Eye (/400 cm2) ≤ | | | | |
Plasticizer absorption of 100g resin ≥ | | | | |
Whiteness (160°C, after 10 min.) % ≥ | | | | |
| | | | | |
Application:
1156: Foam wallpaper, foam floor tile, rotary foaming.
1302: Foam floor, plastic material high bright coating chemical.
1702: Non-foaming artificial leather bottom, surface of artificial leather and floor leather, canvas, maceration forming (gloves, boots), rotary forming (toy), hollow forming and rubber, bottle caps
SG3 is for films, hoses, leathers, wire cables and other general purpose soft products.
SG5 is for pipes, fittings, panels, calendaring, injection, moulding, profiles, and sandals
SG7 / SG8 is for bottles, sheets, calendaring, rigid injection and moulding pipes.
Package:
PVC Resin By 25kgs/pp bag 17mt per 20'fcl 26mt per 40'fcl
PVC Resin Paste By 20 kg bag, 12 tons/20’GP, 25 tons/40’GP
Product Categories : Resin > Pvc Resin