Tio2 Titanium Dioxido De Cloro R900 R105 Type
Titanium Dioxide is an odorless white powder. Tasteless. pH 7.5. Occurs in three crystalline forms.Titanium dioxide is a titanium oxide with the formula TiO2. A naturally occurring oxide sourced from ilmenite, rutile and anatase, it has a wide range of applications. It has a role as a food colouring.Titanium dioxide, also known as titanium(IV) oxide or titania, is the naturally occurring oxide of titanium. It is used as a pigment under the names titanium white, Pigment White 6 (PW6), or CI 77891. It is typically extracted from ilmenite, rutile and anatase.
Besides, we also supply Iron Oxide,Carbon Black,Chrome Green,Petroleum Resin etc. for different industries,Pigment,Detergent,Plastic,Textile etc.
TECHNICAL DATA SHEET
R-996 is Zirconia and Alumina treated rutile Titanium Dioxide Pigment. It is proved to have excellent outdoor durability and super gloss in paint
& coating，ink and plastic industries.
| TYPE | R-996 |
| Crystal Form | Rutile |
| Classification ISO591，DIN55912 | R2 |
| ASTM D476 | Ⅱ |
| CAS No. | 13463-67-7 |
| TiO2 Content(%) min | 94 |
| pH Value | 6.5~8.5 |
| Density(g/cm3) | 4.1 |
| Oil Absorption (g/100g) max | 22 |
| Specific Resistance(Ωm) min | 150 |
| Average Particle Size(μm) | 0.23 |
| Surface Treatment | Zirconia & Alumina，Organic |
The information in this publication is,to be best of our knowledge,true but since the conditions of use are beyond our control,the values provided
are not to be considered as a warranty or to be implied in respect of such information.
In every case caution must be exercised to avoid violation or infringement of statutory obligations and any rights belonging to a third party.
We are willing to study customer specific outlets involving our products in order to enable their most effective use.
COMPARABLE PRODUCT TEST REPORT
COATING SOLUTIONS：
Alkyd MELAMINE Enamel Test：
Binder 32% coconut alkyd / butylated melamine=70/30 (solid)
Grinding Red Devil 5400 Paint Conditioner
Enamel Dry PVC 24%，Pig / Binder solid=1.2
Coating For Gloss and Color evaluation，coated with 150 micron wet thick applicator on a glassplate and baked for 20 minutes at 130 degree
Centigrade.
For Opacity evaluation，coated with 60 micron wet thick Barcoater on a black and white paper.
| | R-996 | Competitive A | Competitive B | Competitive C |
| Fineness of grinding | (μm) | (μm) | (μm) | (μm) |
| For 3 min | 17 | 20 | 17 | 15 |
| 9 min | 14 | 17 | 13 | 12 |
| 15min | 12 | 16 | 12 | 10 |
| 21min | 10 | 15 | 10 | 8 |
| 40min | <5 | 12 | <5 | <5 |
| 60 Specular Gloss | 89 | 87 | 89 | 90 |
| Color | | | | |
| L | 93.9 | 93.7 | 94.0 | 94.0 |
| a | -1.0 | -0.9 | -0.9 | -1.0 |
| b | 0.6 | 1.2 | 0.8 | 0.9 |
| Whiteness | 93.8 | 93.5 | 93.9 | 93.8 |
| Opacity | | | | |
| Y on black substrate | 75.6 | 74.7 | 75.8 | 75.7 |
| Y on white substrate | 84.7 | 83.9 | 84.8 | 84.5 |
| Contrast Ratio | 89.3 | 89.1 | 89.4 | 89.6 |
APPLICATIONS
R-996 is recommended as a premium pigment for a variety of high quality powder coatings，water-born and solvent-born industrial and
decorative coating，ink and plastics.
PACKING & TRANSPORTION
25KG, 500KG and1000KG, seaworthy and suitable for container transportation
Product Categories : Pigment&Dye > Titanium Dioxide