Titanium Dioxide Pfr209 For Glass And PVC Pipe
Titanium dioxide has three crystal forms in nature: rutile, anatase and brookite. The brookite type belongs to the orthorhombic crystal system and is an unstable crystal type. It is transformed into a rutile type at a temperature above 650°C, so it has no practical value in industry. Anatase is stable at room temperature, but it needs to transform to rutile at high temperature. The conversion strength depends on the manufacturing method and whether there are inhibitors or accelerators added during the calcination process.
TECHNICAL DATA SHEET
R-996 is Zirconia and Alumina treated rutile Titanium Dioxide Pigment. It is proved to have excellent outdoor durability and super gloss in paint
& coating，ink and plastic industries.
| TYPE | R-996 |
| Crystal Form | Rutile |
| Classification ISO591，DIN55912 | R2 |
| ASTM D476 | Ⅱ |
| CAS No. | 13463-67-7 |
| TiO2 Content(%) min | 94 |
| pH Value | 6.5~8.5 |
| Density(g/cm3) | 4.1 |
| Oil Absorption (g/100g) max | 22 |
| Specific Resistance(Ωm) min | 150 |
| Average Particle Size(μm) | 0.23 |
| Surface Treatment | Zirconia & Alumina，Organic |
The information in this publication is,to be best of our knowledge,true but since the conditions of use are beyond our control,the values provided
are not to be considered as a warranty or to be implied in respect of such information.
In every case caution must be exercised to avoid violation or infringement of statutory obligations and any rights belonging to a third party.
We are willing to study customer specific outlets involving our products in order to enable their most effective use.
Contact: eleven(2)jinhetec.com
whatsapp:008615939012283 katrina
Besides, we also supply Iron Oxide,Carbon Black,Chrome Green,Petroleum Resin etc. for different industries,Pigment,Detergent,Plastic,Textile etc.
COMPARABLE PRODUCT TEST REPORT
COATING SOLUTIONS：
Alkyd MELAMINE Enamel Test：
Binder 32% coconut alkyd / butylated melamine=70/30 (solid)
Grinding Red Devil 5400 Paint Conditioner
Enamel Dry PVC 24%，Pig / Binder solid=1.2
Coating For Gloss and Color evaluation，coated with 150 micron wet thick applicator on a glassplate and baked for 20 minutes at 130 degree
Centigrade.
For Opacity evaluation，coated with 60 micron wet thick Barcoater on a black and white paper.
| | R-996 | Competitive A | Competitive B | Competitive C |
| Fineness of grinding | (μm) | (μm) | (μm) | (μm) |
| For 3 min | 17 | 20 | 17 | 15 |
| 9 min | 14 | 17 | 13 | 12 |
| 15min | 12 | 16 | 12 | 10 |
| 21min | 10 | 15 | 10 | 8 |
| 40min | <5 | 12 | <5 | <5 |
| 60 Specular Gloss | 89 | 87 | 89 | 90 |
| Color | | | | |
| L | 93.9 | 93.7 | 94.0 | 94.0 |
| a | -1.0 | -0.9 | -0.9 | -1.0 |
| b | 0.6 | 1.2 | 0.8 | 0.9 |
| Whiteness | 93.8 | 93.5 | 93.9 | 93.8 |
| Opacity | | | | |
| Y on black substrate | 75.6 | 74.7 | 75.8 | 75.7 |
| Y on white substrate | 84.7 | 83.9 | 84.8 | 84.5 |
| Contrast Ratio | 89.3 | 89.1 | 89.4 | 89.6 |
APPLICATIONS
R-996 is recommended as a premium pigment for a variety of high quality powder coatings，water-born and solvent-born industrial and
decorative coating，ink and plastics.