Sinopec PVA 088-50 For Polymerization Additive
Discription:
PVA has good adhesion to hydrophilic cellulose. In general, the higher the degree of polymerization and alcoholysis, the stronger the bond strength. When the thermally stable PVA powder is heated to about 100°C, the appearance gradually changes. The partially alcoholyzed PVA begins to melt at around 190°C and decomposes at 200°C. Complete alcoholysis of PVA begins to melt at about 230°C, and decomposes at 240°C. Thermal cracking experiments show that the lower the degree of polymerization, the faster the weight loss; the higher the degree of alcoholysis, the shorter the decomposition time.
Specification:
| Items | Degree of alcoholysis (Mol)% | viscosity (mPa.s) | Volatile content % ≤ | ash content % ≤ | pH | Purity % ≥ |
| 100-27S | 99.5～100.0 | 23.0～29.0 | 6.0 | 0.8 | - | 92.0 |
| 100-40 | 99.5～100.0 | 35.0～45.0 | 6.0 | 0.8 | - | 92.0 |
| 100-78 | 99.5～100.0 | 73.0～83.0 | 6.0 | 0.8 | - | 92.0 |
| 098-03 | 98.0～98.8 | 3.2～4.0 | 5.0 | 0.7 | 5.0～7.0 | 94.0 |
| 098-04 | 98.0～98.8 | 4.0～5.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-10 | 98.0～98.8 | 8.0～12.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-15 | 98.0～98.8 | 13.0～17.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-20 | 98.0～98.8 | 18.0～22.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-27 | 98.0～98.8 | 23.0～29.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 098-30 | 98.0～98.8 | 28.0～32.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 097-29 | 96.0～98.0 | 27.0～31.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 097-60 | 96.0～98.0 | 56.0～66.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 092-53 | 91.0～93.0 | 48.0～58.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-03 | 86.5～88.5 | 3.0～4.0 | 5.0 | 0.7 | 5.0～7.0 | 94.0 |
| 088-05 | 86.5～88.5 | 4.5～6.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-08 | 86.5～88.5 | 8.0～10.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-13 | 86.5～88.5 | 12.0～14.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-20 | 86.5～88.5 | 21.0～24.5 | 5.0 | 0.4 | 5.0～7.0 | 94.0 |
| 088-26 | 86.5～88.5 | 24.0～28.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-35 | 86.5～88.5 | 29.0～34.0 | 5.0 | 0.3 | 5.0～7.0 | 94.0 |
| 088-40 | 86.5～88.5 | 38.0～42.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-50 | 86.5～88.5 | 45.0～55.0 | 5.0 | 0.3 | 5.0～7.0 | 94.0 |
| 080-44 | 78.0～82.0 | 42.0～52.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 088-60 | 86.5～88.5 | 56.0～66.0 | 5.0 | 0.5 | 5.0～7.0 | 94.0 |
| 086-03 | 85.0～87.0 | 3.4～4.2 | 5.0 | 0.4 | 5～7 | 93.5 |
| 098-05 | 98.0～99.0 | 5.0～6.5 | 5.0 | 0.5 | 5～7 | 93.5 |
| 098-08 | 98.0～99.0 | 9.0～11.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 092-20 | 91.0～93.0 | 21.0～27.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 094-27 | 94.0～96.0 | 22.0～28.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 096-27 | 96.0～98.0 | 23.0～29.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 100-27 | 99.0～100.0 | 22.0～28.0 | 5.0 | 0.7 | / | 93.5 |
| 092-35 | 91.0～93.0 | 30.0～36.0 | 5.0 | 0.3 | 5～7 | 93.5 |
| 100-35 | 99.0～100.0 | 35.0～43.0 | 5.0 | 0.7 | 5～7 | 93.5 |
| 098-60 | 98.0～99.0 | 58.0～68.0 | 5.0 | 0.5 | 5～7 | 93.5 |
| 100-60 | 99.0～100.0 | 58.0～68.0 | 5.0 | 0.7 | 5～7 | 93.5 |
| 100-70 | 99.0～100.0 | 68.0～78.0 | 5.0 | 0.7 | 5～7 | 93.5 |
Packing:
paper-plastic composite bag, with plastic film inner bag, net weight of each bag is 20kg&25kg.
Application:
Mainly used in textile pulp, paper binder, rewetting binder, surface sizing agent for paper, pigment carrier, Adhesives for architectural coatings, adhesives and additives for building materials, coating agents for seeds and pharmaceuticals, adhesives for inorganic and electronic products, Water-soluble film, cosmetic additive, stabilizer for vinyl acetate emulsion polymerization and vinyl chloride suspension polymerization, temporary protective film etc.